Silver nanoparticle

Silver nanoparticles are nanoparticles of silver of between 1 nm and 100 nm in size. While frequently described as being 'silver' some are composed of a large percentage of silver oxide due to their large ratio of surface-to-bulk silver atoms. Numerous shapes of nanoparticles can be constructed depending on the application at hand. Commonly used are spherical silver nanoparticles but diamond, octagonal and thin sheets are also popular. grapefruit-sized device alongside the tub uses electrical currents to nanoshave two silver plates the size of large chewing gum sticks. Resulting in positively charged silver atoms-silver ions (Ag+)-are injected into the tub during the wash cycle. Silver nanoparticles are nanoparticles of silver of between 1 nm and 100 nm in size. While frequently described as being 'silver' some are composed of a large percentage of silver oxide due to their large ratio of surface-to-bulk silver atoms. Numerous shapes of nanoparticles can be constructed depending on the application at hand. Commonly used are spherical silver nanoparticles but diamond, octagonal and thin sheets are also popular. Their extremely large surface area permits the coordination of a vast number of ligands. The properties of silver nanoparticles applicable to human treatments are under investigation in laboratory and animal studies, assessing potential efficacy, toxicity, and costs. The most common methods for nanoparticle synthesis fall under the category of wet chemistry, or the nucleation of particles within a solution. This nucleation occurs when a silver ion complex, usually AgNO3 or AgClO4, is reduced to colloidal silver in the presence of a reducing agent. When the concentration increases enough, dissolved metallic silver ions bind together to form a stable surface. The surface is energetically unfavorable when the cluster is small, because the energy gained by decreasing the concentration of dissolved particles is not as high as the energy lost from creating a new surface. When the cluster reaches a certain size, known as the critical radius, it becomes energetically favorable, and thus stable enough to continue to grow. This nucleus then remains in the system and grows as more silver atoms diffuse through the solution and attach to the surface When the dissolved concentration of atomic silver decreases enough, it is no longer possible for enough atoms to bind together to form a stable nucleus. At this nucleation threshold, new nanoparticles stop being formed, and the remaining dissolved silver is absorbed by diffusion into the growing nanoparticles in the solution. As the particles grow, other molecules in the solution diffuse and attach to the surface. This process stabilizes the surface energy of the particle and blocks new silver ions from reaching the surface. The attachment of these capping/stabilizing agents slows and eventually stops the growth of the particle. The most common capping ligands are trisodium citrate and polyvinylpyrrolidone (PVP), but many others are also used in varying conditions to synthesize particles with particular sizes, shapes, and surface properties. There are many different wet synthesis methods, including the use of reducing sugars, citrate reduction, reduction via sodium borohydride, the silver mirror reaction, the polyol process, seed-mediated growth, and light-mediated growth. Each of these methods, or a combination of methods, will offer differing degrees of control over the size distribution as well as distributions of geometric arrangements of the nanoparticle. A new, very promising wet-chemical technique was found by Elsupikhe et al. (2015). They have developed a green ultrasonically-assisted synthesis. Under ultrasound treatment, silver nanoparticles (AgNP) are synthesized with κ-carrageenan as a natural stabilizer. The reaction is performed at ambient temperature and produces silver nanoparticles with fcc crystal structure without impurities. The concentration of κ-carrageenan is used to influence particle size distribution of the AgNPs. There are many ways silver nanoparticles can be synthesized; one method is through monosaccharides. This includes glucose, fructose, maltose, maltodextrin, etc. but not sucrose. It is also a simple method to reduce silver ions back to silver nanoparticles as it usually involves a one-step process. There have been methods that indicated that these reducing sugars are essential to the formation of silver nanoparticles. Many studies indicated that this method of green synthesis, specifically using Cacumen platycladi extract, enabled the reduction of silver. Additionally, the size of the nanoparticle could be controlled depending on the concentration of the extract. The studies indicate that the higher concentrations correlated to an increased number of nanoparticles. Smaller nanoparticles were formed at high pH levels due to the concentration of the monosaccharides. Another method of silver nanoparticle synthesis includes the use of reducing sugars with alkali starch and silver nitrate. The reducing sugars have free aldehyde and ketone groups, which enable them to be oxidized into gluconate. The monosaccharide must have a free ketone group because in order to act as a reducing agent it first undergoes tautomerization. In addition, if the aldehydes are bound, it will be stuck in cyclic form and cannot act as a reducing agent. For example, glucose has an aldehyde functional group that is able to reduce silver cations to silver atoms and is then oxidized to gluconic acid. The reaction for the sugars to be oxidized occurs in aqueous solutions. The capping agent is also not present when heated. An early, and very common, method for synthesizing silver nanoparticles is citrate reduction. This method was first recorded by M. C. Lea, who successfully produced a citrate-stabilized silver colloid in 1889. Citrate reduction involves the reduction of a silver source particle, usually AgNO3 or AgClO4, to colloidal silver using trisodium citrate, Na3C6H5O7. The synthesis is usually performed at an elevated temperature (~100 °C) to maximize the monodispersity (uniformity in both size and shape) of the particle. In this method, the citrate ion traditionally acts as both the reducing agent and the capping ligand, making it a useful process for AgNP production due to its relative ease and short reaction time. However, the silver particles formed may exhibit broad size distributions and form several different particle geometries simultaneously. The addition of stronger reducing agents to the reaction is often used to synthesize particles of a more uniform size and shape.