Misorientation

Misorientation is the difference in crystallographic orientation between two crystallites in a polycrystalline material. Misorientation is the difference in crystallographic orientation between two crystallites in a polycrystalline material. In crystalline materials, the orientation of a crystallite is defined by a transformation from a sample reference frame (i.e. defined by the direction of a rolling or extrusion process and two orthogonal directions) to the local reference frame of the crystalline lattice, as defined by the basis of the unit cell. In the same way, misorientation is the transformation necessary to move from one local crystal frame to some other crystal frame. That is, it is the distance in orientation space between two distinct orientations. If the orientations are specified in terms of matrices of direction cosines gA and gB, then the misorientation operator ∆gAB going from A to B can be defined as follows: where the term gA−1 is the reverse operation of gA, that is, transformation from crystal frame A back to the sample frame. This provides an alternate description of misorientation as the successive operation of transforming from the first crystal frame (A) back to the sample frame and subsequently to the new crystal frame (B). Various methods can be used to represent this transformation operation, such as: Euler angles, Rodrigues vectors, axis/angle (where the axis is specified as a crystallographic direction), or unit quaternions. The effect of crystal symmetry on misorientations is to reduce the fraction of the full orientation space necessary to uniquely represent all possible misorientation relationships. For example, cubic crystals (i.e. FCC) have 24 symmetrically related orientations. Each of these orientations is physically indistinguishable, though mathematically distinct. Therefore, the size of orientation space is reduced by a factor of 24. This defines the fundamental zone (FZ) for cubic symmetries. For the misorientation between two cubic crystallites, each possesses its 24 inherent symmetries. In addition, there exists a switching symmetry, defined by: which recognizes the invariance of misorientation to direction; A→B or B→A. The fraction of the total orientation space in the cubic-cubic fundamental zone for misorientation is then given by: or 1/48 the volume of the cubic fundamental zone. This also has the effect of limiting the maximum unique misorientation angle to 62.8°Disorientation describes the misorientation with the smallest possible rotation angle out of all symmetrically equivalent misorientations that fall within the FZ (usually specified as having an axis in the standard stereographic triangle for cubics). Calculation of these variants involves application of crystal symmetry operators to each of the orientations during the calculation of misorientation. Δ g A B = O B c r y s g B ( O A c r y s g A ) − 1 {displaystyle Delta g_{AB}=O_{B}^{crys}g_{B}(O_{A}^{crys}g_{A})^{-1}} where Ocrys denotes one of the symmetry operators for the material. The misorientation distribution (MD) is analogous to the ODF used in characterizing texture. The MD describes the probability of the misorientation between any two grains falling into a range d Δ g {displaystyle dDelta g} around a given misorientation Δ g {displaystyle Delta g} . While similar to a probability density, the MD is not mathematically the same due to the normalization. The intensity in a MD is given as 'multiples of random density' (MRD) with respect to the distribution expected in a material with uniformly distributed misorientations. The MD can be calculated by either series expansion, typically using generalized spherical harmonics, or by a discrete binning scheme, where each data point is assigned to a bin and accumulated. Discrete misorientations or the misorientation distribution can be fully described as plots in the Euler angle, axis/angle, or Rodrigues vector space. Unit quaternions, while computationally convenient, do not lend themselves to graphical representation because of their four-dimensional nature. For any of the representations, plots are usually constructed as sections through the fundamental zone; along φ2 in Euler angles, at increments of rotation angle for axis/angle, and at constant ρ3 (parallel to <001>) for Rodrigues. Due to the irregular shape of the cubic-cubic FZ, the plots are typically given as sections through the cubic FZ with the more restrictive boundaries overlaid.Mackenzie plots are a one-dimensional representation of the MD plotting the relative frequency of the misorientation angle, irrespective of the axis. Mackenzie determined the misorientation distribution for a cubic sample with a random texture.