Quenching

In materials science, quenching is the rapid cooling of a workpiece in water, oil or air to obtain certain material properties. A type of heat treating, quenching prevents undesired low-temperature processes, such as phase transformations, from occurring. It does this by reducing the window of time during which these undesired reactions are both thermodynamically favorable, and kinetically accessible; for instance, quenching can reduce the crystal grain size of both metallic and plastic materials, increasing their hardness.as when a man who works as a blacksmith plunges a screaming great axe blade or adze into cold water, treating it for temper, since this is the way steel is made strong, even so Cyclops' eye sizzled about the beam of the olive. In materials science, quenching is the rapid cooling of a workpiece in water, oil or air to obtain certain material properties. A type of heat treating, quenching prevents undesired low-temperature processes, such as phase transformations, from occurring. It does this by reducing the window of time during which these undesired reactions are both thermodynamically favorable, and kinetically accessible; for instance, quenching can reduce the crystal grain size of both metallic and plastic materials, increasing their hardness. In metallurgy, quenching is most commonly used to harden steel by introducing martensite, in which case the steel must be rapidly cooled through its eutectoid point, the temperature at which austenite becomes unstable. In steel alloyed with metals such as nickel and manganese, the eutectoid temperature becomes much lower, but the kinetic barriers to phase transformation remain the same. This allows quenching to start at a lower temperature, making the process much easier. High speed steel also has added tungsten, which serves to raise kinetic barriers, which among other effects gives material properties (hardness and abrasion resistance) as though the workpiece had been cooled more rapidly than it really has. Even cooling such alloys slowly in air has most of the desired effects of quenching; high-speed steel weakens much less from heat cycling due to high-speed cutting. Extremely rapid cooling can prevent the formation of all crystal structure, resulting in amorphous metal or 'metallic glass'. Quench hardening is a mechanical process in which steel and cast iron alloys are strengthened and hardened. These metals consist of ferrous metals and alloys. This is done by heating the material to a certain temperature, depending on the material. This produces a harder material by either surface hardening or through-hardening varying on the rate at which the material is cooled. The material is then often tempered to reduce the brittleness that may increase from the quench hardening process. Items that may be quenched include gears, shafts, and wear blocks. Before hardening, cast steels and iron are of a uniform and lamellar (or layered) pearlitic grain structure. This is a mixture of ferrite and cementite formed when steel or cast iron are manufactured and cooled at a slow rate. Pearlite is not an ideal material for many common applications of steel alloys as it is quite soft. By heating pearlite past its eutectoid transition temperature of 727 °C and then rapidly cooling, some of the material’s crystal structure can be transformed into a much harder structure known as martensite. Steels with this martensitic structure are often used in applications when the workpiece must be highly resistant to deformation, such as the cutting edge of blades. This is very efficient.