Magnetic susceptibility of amorphous Cu1−xYx alloys

The magnetic susceptibility of amorphous non-superconducting Cu1−xYx alloys (x = 0.28 and 0.67) is measured in the temperature range 4.2 to 300 K. Alloys are prepared by melt-spinning in nitrogen enriched atmosphere as well as in helium gas. The results for differently prepared samples are similar. The magnitude of the magnetic susceptibility χ is found to be close to that obtained from linear interpolation between the values for crystalline Cu and Y. χ is found to be almost temperature independent in the region 40 to 300 K and to increase with decreasing temperature at low temperatures. The magnetic field dependence of χ is small. Die magnetische Suszeptibilitat der amorphen, nicht-supraleitenden Cu1−xYx Legierungen (x = = 0,28 und 0,67) wird im Temperaturbereich von 4,2 bis 300 K gemessen. Die Proben werden vom flussigen Zustand in stickstoffreicher Atmosphare sowie in Helium schnell abgeschreckt. Die Resultate unterschiedlich hergestellter Proben sind ahnlich. Die magnetische Suszeptibilitat χ der Legierungen ist vergleichbar mit dem Resultat einer linearen Interpolation zwischen kristallinem Cu und Y. χ ist im Bereich von 40 bis 300 K temperaturunabhangig und steigert sich mit sinkender Temperatur bei niedrigeren Temperaturen. Die Magnetfeldabhangigkeit von χ ist gering.