Influence of Zr content on β-phase stability in α-type Ti–Al alloys

Abstract The alloying effect of Zr on β (body-centred cubic)-phase stability was investigated in α (hexagonal close packed)-type Ti–Al alloys. According to calculations and experiments, adding Zr significantly modified the β-phase stability, because Zr was identified as a β-stabilising element in these Ti–Zr–Al alloys under the solution treatment. However, the water-quenched β-phase did not continue to be preserved after aging. In addition, stress-induced α″ (orthorhombic)-phase martensite transformation would occur during deformation.