Microstructural and Mechanical Characterization of W-CuCrZr Joints Brazed with Cu-Ti Filler Alloy

The determination of the mechanical properties of a brazed joint is an important factor to reach the metallurgical level of a joint development. This paper evaluates the mechanical properties, and its correlation with the joint microstructure, of a W-CuCrZr joint brazed in a high vacuum furnace using 80Cu-20Ti flexible filler material in tape form. This joint is meant to be implemented in the divertor application in future fusion power plants. Main experimental parameters were a brazing temperature of 960 °C and a dwell time of 10 min. The microstructure of the joint was constituted by Cu solid solution and Cu4Ti phases. This last phase was distributed in the W-braze interface. Mechanical properties were evaluated by means of Vickers microhardness and mechanical tests by applying pure shear loads. The microhardness profile of the brazed joint indicated that W remained with the as-received hardness but CuCrZr base material was softened after the brazing procedure. Shear strength of 96 ± 15 MPa was obtained for the brazed joint and fracture propagated at the W-braze interface.