Rietveld refinement of the crystal structure of perovskite solar cells using CH3NH3PbI3 and other compounds

The crystal structures of perovskite thin films including CH3NH3PbI3, CH3NH3Pb1-xSbxI3, and CH3NH3PbI3-yCly in the solar cell configuration were studied by using Rietveld refinement. For the CH3NH3PbI3 and CH3NH3Pb1-xSbxI3 samples, satisfactory agreement with the measured profiles was obtained with a weighted profile R−factor (Rwp) of as low as 3%. It was shown that the site occupancy of methylammonium (MA) was decreased in the antimonized cell due to the compensation effect of an increased positive charge brought about by replacing Pb2+ with Sb3+. Photovoltaic measurements showed that the power conversion efficiency was enhanced by adding a small amount of Sb to the CH3NH3PbI3 cell, but it was monotonically decreased as the mole fraction of Sb exceeded 0.03. This variation of the conversion efficiency was considered as a result of suppressed crystallization of PbI2 and carrier recombination via MA vacancies in the antimonized cells. In the case of CH3NH3PbI2.88Cl0.12 sample, the agreement with the measur...