Dielectric and electromechanical properties of rare earth calcium oxyborate piezoelectric crystals at high temperatures
2011
The electrical resistivity, dielectric, and electromechanical properties of ReCa 4 O(BO 3 ) 3 (ReCOB; Re = Er, Y, Gd, Sm, Nd, Pr, and La) piezoelectric crystals were investigated as a function of temperature up to 1000°C. Of the studied crystals, ErCOB and YCOB were found to possess extremely high resistivity (p): p >; 3 × 10 7 ω.cm at 1000°C. The property variation in ReCOB crystals is discussed with respect to their disordered structure. The highest electromechanical coupling factor κ 26 and piezoelectric coefficient d 26 at 1000°C, were achieved in PrCOB crystals, with values being on the order of 24.7% and 13.1 pC/N, respectively. The high thermal stability of the electromechanical properties, with variation less than 25%, together with the low dielectric loss ( ;1500) at elevated temperatures of 1000°C, make ErCOB, YCOB, and GdCOB crystals promising for ultrahigh temperature electromechanical applications.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
22
References
40
Citations
NaN
KQI