CRACK GROWTH BEHAVIOR OF STYRENE-BUTADIENE RUBBER, NATURAL RUBBER, AND POLYBUTADIENE RUBBER COMPOUNDS: COMPARISON OF PURE-SHEAR VERSUS STRIP TENSILE TEST

ABSTRACT Fatigue crack growth experiments on different carbon black–filled rubber compounds have been carried out to evaluate the influence of pure-shear and strip tensile testing mode by using sine and pulse as waveforms. In a previous set of experimental investigations regarding the influence of both waveform and tested material, it was found that the mode I of crack opening sometimes propagates too quickly to be properly monitored in tests involving strip-tensile specimens. An alternative test methodology based on pure-shear test mode has been investigated, optimizing both the shape of the specimen and the test equipment. Data obtained from the different compound formulations were consistent with the theoretical background and resulted in similar ranking of compound crack growth resistance for the two testing modes; in addition, pure-shear mode showed a higher sensitivity to formula variations.