Investigation of the workability and surface roughness of thin brass wires in various dieless drawing technologies

Possibilities of improving the workability of the CuZn37 brass thin wire in a diameter of 0.14–0.18 mm produced by the dieless drawing processes were explored. The workability was defined as the maximum final longitudinal strain of the wire up to its fracture, achievable in the dieless drawing process. Two technologies of dieless drawing were developed and their workability was compared. The first one is the classical one-pass process; the second, a multi-pass one. For both developed technologies, it was possible to obtain a good-quality product but more than two times higher workability has been demonstrated for the multi-pass technology. No evident effect of the deformation temperature from the window of technologically accepted parameters on the workability was found but an increase in the temperature significantly increased the roughness of the product surface. For the same deformation temperature, the roughness of the wire obtained from the multi-pass process appeared to be significantly lower than for the one of the classical one-pass technologies.