The effects of carbon on the phase stability and mechanical properties of heat-treated FeNiMnCrAl high entropy alloys

Abstract This work systematically investigates the effect of carbon on the phase stability and room- temperature tensile performance of an annealed Fe 40.4 Ni 11.3 Mn 34.8 Al 7.5 Cr 6 (at%) high entropy alloy without (HEA) and with 1.1% carbon (CHEA). Four annealing conditions were investigated: 773 K for 13 d and 42 d, 973 K for 20 d, and 1073 K and 1423 K for 24 h. The resulting microstructures were analyzed using a combination of scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive spectroscopy (EDS), and atom probe tomography (APT). Vickers hardness testing and room- temperature tensile testing were used to determine the mechanical properties of the annealed HEA and the CHEA. APT composition profiles revealed fine Ni,Mn,Al-enriched matrix precipitates in the CHEA annealed at 773 K for 13 d. After ageing at 773 K for 42 d, colonies of (Ni,Fe) 2 MnAl- enriched Heusler phase lamellae were observed at the grain boundaries (GBs) and in the matrix for the HEA, while GB lamellar colonies of Mn,Cr-enriched M 23 C 6 carbides were observed for the CHEA. Due to the presence of the GB carbides, the resulting room-temperature elongation to fracture for the CHEA annealed at 773 K for 42 d was ~1% compared to ~11% for the HEA given the same anneal. At higher annealing temperatures, the microstructure contains Ni,Al-rich and Mn,Cr,C-rich precipitates that alternate along the GBs and appear to be associated with each other in the matrix. Electron diffraction analysis indicates the aforementioned Ni,Al-precipitates and Mn,Cr-carbides have b.c.c. and f.c.c. crystal structures, respectively. Once again, a low elongation to fracture (2%) was seen for the carbon-containing material compared to its un-doped counterpart (23%) which solely contained Ni,Al-rich b.c.c. precipitates.