Microstructure and trapped field of YBCO bulk single-grain superconductors prepared by interior seeding

The microstructural analyses of YBCO bulk single-grain superconductors grown by interior seeding with taller and shorter upper pellets have shown that a suitable upper pellet height can lower the porosity in the upper part of the sample, produce a more appropriate distribution of pinning centres in the form of Y-211 particles and suppress subgrain formation with a higher crystal misalignment in the c-growth sector (c-GS), which can lead to a higher measured trapped magnetic field and a more uniform cone of the trapped-field profile. The observed bulging of the sample surface at the c-GS can be explained by the edge melt distribution model, which shows that macroscopic mass transport to the growth sector occurs with higher growth rates.