Study of LCF Behavior of IN718 Superalloy at Room Temperature

nconel 718 is an age hardenable nickel base supper alloy with high strength at elevated temperatures, and excellent creep properties. It is used extensively in turbine discs, blades where components experience elevated temperatures for prolonged duration, leading to coarsening of the microstructure. To evaluate the life of such components after prolonged exposure to service conditions, LCF properties at such large grain sizes are essential. For this purpose, low cycle fatigue (LCF) behavior of forged Inconel 718 turbine rotor disc having large grain size was studied at room temperature. Total strain controlled fatigue tests were conducted in air at ambient temperature on this alloy in solution treated and aged condition. The results indicated that the material exhibits cyclic strain softening and the cyclic yield strength is lower by 40% compared to the monotonic yield strength. The deformation takes place by multiple planar slip.