Martensitic transformation in Heusler alloys Mn2YIn (Y=Ni, Pd and Pt): Theoretical and experimental investigation

Abstract The martensitic transformation and electronic structure of Heusler alloys Mn 2 YIn (Y=Ni, Pd, Pt) have been investigated by both first-principles calculation and experimental investigation. Theoretical calculation reveals that, the energy difference Δ E between the tetragonal martensitic phase and cubic austenitic phase increases with Y varying from Ni to Pt in Mn 2 YIn. Thus a structural transition from cubic to tetragonal is most likely to happen in Heusler alloy Mn 2 PtIn. A single Heusler phase can be obtained in both Mn 2 PtIn and Mn 2 PdIn. A martensitic transformation temperature of 615 K has been identified in Mn 2 PtIn. And in Mn 2 PdIn, the austenitic phase is stable and no martensitic transformation is observed till 5 K. This indicates there may exist a positive relation between Δ E and martensitic transformation temperature. Calculated results show that Mn 2 YIn are all ferrimagnets in both austenitic and martensitic phases. The magnetic properties are mainly determined by the antiparallel aligned Mn spin moments. These findings can help to develop new FSMAs with novel properties.