Effect of Cu content on exfoliation corrosion and electrochemical corrosion of A7N01 aluminum alloy in EXCO solution

The exfoliation corrosion (EXCO) sensitivities and electrochemical corrosions of A7N01 aluminum (Al) alloys with 0.074% and 0.136% Cu contents were investigated in EXCO solution. The exfoliation corrosion developed more rapidly for the alloy with 0.136% Cu by expressing higher exfoliation rate and deeper corrosion pits as observed by SEM and laser confocal scanning microscopy (LCSM). In EXCO solution, the alloy with 0.136% Cu content showed lower open-circuit potential (OCP) than the alloy with 0.074% Cu content. The alloy with 0.136% Cu content had bigger “hysteresis loop” in cyclic polarization curve which meant lower self-passivation ability. In electrochemical impedance spectroscopy plot, its curvature radius and capacitance index were lower. The electrochemical test results revealed that the alloy with 0.136% Cu content showed more severe electrochemical corrosion than the alloy with 0.074% Cu content, consistent with the exfoliation corrosion results. The microstructures of two alloys were observed through optical microscopy (OM) and transmission electron microscopy (TEM). The continuous distribution of the equilibrium precipitate η-MgZn2 on grain boundaries, the decreasing of the width of precipitate-free zone (PFZ) and the coarse Cu–Fe–Si–rich phase were responsible for the higher corrosion sensitivity of the Al alloy with 0.136% Cu than that of Al alloy with 0.074% Cu content in EXCO solution.