Tuning the Surface Characteristic of Al-Si Alloys and Its Impacts on the Formation of Micro Arc Oxidation Layers

2021 
Aluminum Silicon (Al-Si) alloys are the most important among cast alloys and have widespread application. The β-Si phase is detrimental to the growth of micro arc oxidation (MAO) layers on Al-Si alloys. In this paper, the β-Si in the skin layer of different Al-Si alloys was removed by an acid etching pretreatment. Then, the impacts of different etching condition on their MAO process were investigated. Results show that, as etching time was prolonged, the Si content on the surface of Al-12 Si was decreased greatly (less than 0.5 wt.%), and the average size of pores left on the sample surface was increased gradually. This then led to the occurrence of some bigger and more drastic discharge sparks at the earlier oxidation stage. The corresponding layers had a higher ratio of Al2O3 and better corrosion resistance after 30 min of oxidation. Moreover, a 60 s etching pretreatment benefitted and boosted the growth rate and energy efficiency of layers on the Al-9 Si, Al-12 Si and Al-15 Si alloys. Such pretreatment was believed to be applicable to restrain the negative effects of Si on the MAO of different Al-Si alloys.
    • Correction
    • Source
    • Cite
    • Save
    • Machine Reading By IdeaReader
    26
    References
    0
    Citations
    NaN
    KQI
    []