Evaluation of a new test method to determine the failure mode and macro-shear bond strength of dental materials to metals

Objective: To compare the macro mean shear bond strength (SBS) and failure mode of three cements to two types of metal using mould-enclosed and non-enclosed cement specimens. Methods: Titanium and base metal cobalt-based substrates were finished with 50 μm aluminium oxide. Two resin-modified glass-ionomers (Riva Luting Plus, Fuji Plus) and one resin cement (RelyX Unicem) were prepared as per manufacturers’ instructions. Metal mould-enclosed and non-enclosed cement specimens with a bonding area diameter of 3.5 mm were prepared and stressed to failure using a 2 mm blunt edge shear knife at a cross-head speed of 1 mm/min to determine mean SBS. The shear knife was placed against the surface of the substrate. Failure analysis of the failed interface was performed with a stereo microscope at 40× magnification. Results: Two-way Analysis of Variance demonstrated a significant difference in mean SBS between materials (p = 0.004) and cement (p = 0.001). There was also a significant interaction between method and ce...