Preparation of phosphorus-modified PITQ-13 catalysts and their performance in 1-butene catalytic cracking

Abstract A series of phosphorus-modified PITQ-13 catalysts was prepared by wet impregnation of NH 4 H 2 PO 4 solution into an HITQ-13 parent. The catalysts were characterized using XRD, N 2 adsorption, MAS NMR and NH 3 -TPD. Their catalytic performance in 1-butene catalytic cracking was evaluated in a fixed fluidized bed reactor. The results showed that the crystallinity, surface area and pore volume of P-modified PITQ-13 catalysts decreased with the increasing amounts of P. The number of weak acid sites increased, whereas that of strong acidity decreased. The selectivity to propylene in 1-butene cracking reactions increased because of the decrease in strong acidity. The yield of propylene achieved 41.6% over PITQ-13-2 catalyst with a P content of 1.0 wt%, which was 5.1% greater than that achieved over HITQ-13 catalyst.