Microstructure and Mechanical Properties of the Cold-Rolled Mg-14Li-1Zn Alloy after Hot Rolling
2019
The as-cast Mg-14Li-1Zn alloy was hot rolled at different temperatures with the reduction of 50%, followed by cold rolling with the reduction of 80%. The effects of the hot rolling temperature on the microstructure and mechanical properties of the final specimens were investigated. The results show that the higher rolling temperature brings about a more homogeneous microstructure, which is favorable for the subsequent cold rolling. When the hot rolling temperature is 300°C, the final specimen possesses the highest tensile strength and hardness of 238 MPa and 67.7 HV, respectively. When the hot rolling temperature is 200°C, the final specimen possesses the highest elongation of 24.6%.