Preparation and Properties of Silane-Terminated Poly(urethane-Imide)

A serious of silane-terminated poly (urethane-imide) (Si-PUI) was synthesized via prepolymer method using polycarbonatediols (PCDL), 2,4-tolylene diisocyanate (TDI), 4,4'-Oxydiphthalic Anhydride (ODPA) and silane coupling agent KH-550. The structure of the products was characterized by FT-IR. The thermal properties were measured by thermal gravimetric analysis (TGA). The thermal mechanical behavior was investigated by dynamic mechanical analysis (DMA).The mechanical characteristic was measured by tensile tests. The water absorption (Wa) was also been tested. With the imide content increasing, the thermal stability, tensile strength and storage modulus of poly (urethane-imide) improve significantly, and the glass transition temperature rises. The introduction of silanes improves the water resistance and further enhances the thermal stability of poly (urethane-imide).