Evidence for Symmetry Reduction in Ti3(Al1−δCuδ)C2 MAX Phase Solid Solutions
2017
Ti3[Al1−δCuδ]C2 MAX phase solid solutions have been synthesized by sintering compacted Ti3AlC2–Cu composites produced by mechanical milling. Using X-ray and neutron diffraction techniques, it is demonstrated that the Cu mixing into the Al site is accompanied by lattice distortion, which leads to symmetry reduction from a hexagonal to a monoclinic structure. Such symmetry reduction likely results from this mixing through deviation of the A-site position from the special (0, 0, 1/4) position within the P63/mmc space group of the original Ti3AlC2 structure. Moreover, it is demonstrated that the Cu admixture into the A site can be adjusted from the composition of the reactant mixture. The lattice parameter variation of the solid solution compounds, with 10–50 atom % Cu in the A site, is found to be consistent with Vegard’s law.