Coloring effect of iron oxide content on ceramic glazes and their comparison with the similar waste containing materials

Abstract The effects of adding iron oxide to ceramic glaze formulations were studied in this study. Iron oxide was added in different weight ratios into the reactive transparent glaze, reactive opaque glaze, and transparent glaze formulations. The iron oxide content in the glaze composition, the coloring mechanisms, the phase distributions, and surface properties at temperatures of 950–1000-1050-1200 °C in the oxidation firing medium were investigated. Scanning Electron Microscopy (SEM) to determine the microstructural and morphological characterizations of the test glazes, X-Ray Diffractometry (XRD) to determine the crystallographic properties and phases, and X-Ray Fluorescence (XRF) analyses to determine the elemental and chemical composition were performed. In addition to these, surface images were examined with Digital Microscope (DM) and Commission Internationale de l'Eclairage (CIE) L*a*b, and water absorption values were compared. In addition, taking into account environmental factors, a comparison of ceramic glazes with the same amount of waste iron oxide was also performed for same purpose. As a result of the studies, it was observed that the addition of iron oxide and/or waste iron oxide did not have a negative effect, and coloring effects on the glaze layer were observed at different rates and firing temperatures.