Study on the Phase Selection and Debye Temperature of Hyper-Peritectic Al-Ni Alloy under High Pressure

The phase selection of hyper-peritectic Al-47wt.%Ni alloy solidified under different pressures was investigated. The results show that Al3Ni2 and Al3Ni phases coexist at ambient pressure, while another new phase α-Al exists simultaneously when solidified at high pressure. Based on the competitive growth theory of dendrite, a kinetic stabilization of metastable peritectic phases with respect to stable ones is predicted for different solidification pressures. It demonstrates that Al3Ni2 phase nucleates and grows directly from the undercooled liquid. Meanwhile, the Debye temperatures of Al-47wt.%Ni alloy that fabricated at different pressures were also calculated using the low temperature heat capacity curve.