Ion Channeling Analysis of Gallium Nitride Implanted with Deuterium

Ion channeling and transmission electron microscopy were used to examine the microstructure of GaN implanted with deuterium (D) at high (>1 at. %) and low (< 0.1 at. %) D concentrations. At high concentrations, bubbles and basal-plane stacking faults were observed. Ion channeling showed the D was disordered relative to the GaN lattice, consistent with precipitation of D2 into bubbles. At low D concentrations, bubbles and stacking faults are absent and ion channeling shows that a large fraction of the D occupies sites near the center of the c-axis channel.