Dopant penetration studies through Hf silicate

We present a study of the penetration of B, P, and As through Hf silicate (HfSixOy) and the effect of N incorporation in Hf silicate (HfSixOyNz) on dopant penetration from doped polycrystalline silicon capping layers. The extent of penetration through Hf silicate was found to be dependent upon the thermal annealing budget for each dopant investigated as follows: B(T⩾950°C∕60s), P(T⩾1000°C∕20s), and As (T⩾1050°C∕60s). We propose that the enhanced diffusion observed for these dopants in HfSixOy, compared with that of SiO2 films, is related to grain boundary formation resulting from HfSixOy film crystallization. We also find that, as in the case of SiO2, N incorporation inhibits dopant (B, P, and As) diffusion through the Hf silicate and thus penetration into the underlying Si substrate. Only B penetration is clearly observed through HfSiON films for anneals at 1050 °C for durations of 10 s or longer. The calculated B diffusivity through the HfSixOyNz layer is D0=5.2×10−15cm2∕s.