Domain formation mechanism of the Si(110)\16 2" reconstruction

The main factor that determines which of the two domains form upon reconstruction of the Si(110)"16 x 2" surface has been investigated. LEED and STM images showed that the domain orientation was independent of the heating current direction used to induce the Si(110)"16 x 2" reconstruction. Reciprocal-space lattice models of the reconstruction allowed for the correct identification of the domain orientations in the LEED images and confirm that the reconstruction is 2D-chiral. It is proposed that the domain orientation upon surface reconstruction is determined by the direction of monoatomic steps present on the Si(110) plane. This is in turn determined by the direction at which the surface is polished off-axis from the (110) plane.