Carrier recombination and diffusion in high-purity diamond after electron irradiation and annealing

Carrier-transport mechanisms are studied in high-purity diamond irradiated with 6 MeV electrons in the dose range of 1012–1016 cm−2 and annealed at different temperatures up to 1450 °C. Lifetimes and diffusion coefficients are extracted using two pump–probe techniques based on free-carrier absorption and transient-grating principles and then correlated with the corresponding defect evolution from spectroscopic measurements. The neutral monovacancy is revealed as the main carrier recombination center in the as-irradiated diamond, providing bipolar carrier lifetimes of a few nanoseconds at the highest irradiation dose. Carrier-capture cross sections are reduced during annealing as vacancies aggregate into divacancies at ≤1000 °C and extended vacancy clusters at 1450 °C.