Investigation on hydrogenation performance of Mg2Ni+10 wt.% NbN composite

The Mg{sub 2}Ni+10 wt.% NbN composite was prepared by mechanical milling and its hydrogen absorption/desorption properties and microstructure were systematically investigated. XRD results indicated that NbN was stable during ball milling process while partly decomposed into NbN{sub 0.95} and NbH during hydriding/dehydriding cycles irreversibly. The composite exhibited excellent hydrogenation/dehydrogenation kinetics performance with 2.71 wt.% hydrogen absorbed in 60 s at 423 K and 0.81 wt.% hydrogen released in 2 h at 523 K, respectively. The H diffusion constant of the composite reached 14.98×10{sup −5} s{sup −1} which was more than twice increased than that of pure Mg{sub 2}Ni powder. The superior hydrogen storage properties of the composite were ascribed to the refined grain size and abundant N-defect points provided by NbN and NbN{sub 0.95} in the composite. - Graphical abstract: The Mg{sub 2}Ni+10 wt.% NbN composite displays improvements on particle size distribution as well as hydrogen storage properties compared with that of pure Mg{sub 2}Ni. - Highlights: • NbN is introduced into Mg{sub 2}Ni hydride by Ar protected ball-milling. • Surfaces of the additive NbN particle are reduced by Mg{sub 2}NiH{sub 4}. • Hydrogenation kinetic property at 423 K is double improved. • Dehydrogenation capacity at 523 K of compositesmore » is beyond double improved.« less