Etching of fused silica fiber by metallic laser-induced backside wet etching technique
2013
Abstract The tip of multimode fused silica fiber (core diameter: 550 μm) was etched by metallic laser-induced backside wet etching (M-LIBWE) method. Frequency doubled, Q-switched Nd:YAG laser ( λ = 532 nm; τ FWHM = 8 ns) was used as laser source. The laser beam was coupled into the fiber by a fused silica lens with a focal length of 1500 mm. The other tip of the fiber was dipped into liquid gallium metallic absorber. The etching threshold fluence was measured to be 475 mJ/cm 2 , while the highest fluence, which resulted etching without breaking the fiber, was 1060 mJ/cm 2 . The progress of etching was followed by optical microscopy, and the etch rate was measured to be between 20 and 37 nm/pulse depending on the applied laser energy. The surface morphologies of the etched tips were studied by scanning electron microscopy. A possible application of the structured fibers was also tested.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
47
References
2
Citations
NaN
KQI