Atomically designed precursors in optical fiber amplifiers: The thermal stability of the heterobimetallic ErAl3(OPri)12 in a solution-coated silica soot

The thermal stability of the bimetallic alkoxide ErAl3(OPri)12 doped in an unsintered silica (soot) has been investigated. Samples have been heated to different temperatures (up to 1500°C and analyzed by using ultraviolet-visible-near infrared absorption spectroscopy, infrared spectroscopy, scanning electron microscopy, energy dispersive spectroscopy, thermal gravimetric analysis, and powder x-ray diffraction. It is seen that the doped samples heated up to 1000°C show broad glasslike absorption spectra, indicating an amorphous structure, while the high-temperature sample shows an ordered crystallinelike structure with sharp characteristic absorption peaks. X-ray diffraction measurements indicate the formation of an ordered structure at temperatures of 1500°C, revealing a crystal phase of silica and phases of erbium and aluminosilicate. A comparison is also made with a sample doped with aqueous ErCl3 and Al(NO3)3. It is concluded that the local structure of the ErAl3 precursor is not preserved at temperatu...