Phase formation and performance of solid state reactive sintered Ce0.8Gd0.2O2−δ - FeCo2O4 composites

Reactive sintering of dual phase composites for the use as oxygen transport membrane is a promising method enabling lower sintering temperatures as well as low cost raw materials. Ce0.8Gd0.2O2−δ - FeCo2O4 composites with different nominal weight ratios from 60:40 to 90:10 are processed by reactive sintering of commercial Ce0.8Gd0.2O2−δ, Fe2O3, and Co3O4 powders. The phases formed in-situ during sintering are investigated qualitatively and quantitatively by means of XRD and Rietveld refinement as well as transmission electron microscopy. Besides gadolinia-doped ceria two Fe/Co-spinel phases are in equilibrium in agreement with the phase diagram. Moreover, a donor-doped GdFeO3-based perovskite (Gd,Ce)(Fe,Co)O3 showing electronic conductivity is formed. Due to these intense phase reactions, the composition of each individual phase is assessed for all composites and their functional properties are discussed. The oxygen permeation performances of the composites are measured in dependence of temperature and the potential limiting steps are discussed. The results reveal that the phase reactions support the formation of the desired mixed ionic electronic conductivity achieving percolation at low nominal spinel contents. The specific microstructure plays an extremely important role in the membrane performance and, thus, special attention should be laid on this in future research about dual phase membranes.