Ductility recovery in structural materials for spallation targets by post-irradiation annealing

Abstract Low temperature irradiation embrittlement is one of the major criteria to determine the lifetime of spallation targets. Embrittlement is especially high at low service temperatures, e.g. 250 °C in liquid-mercury sources. It was the aim of the present study to investigate the effect of post-irradiation annealing on the mechanical properties of irradiated structural materials. The specimens used were obtained from spent target components of operating spallation facilities (Los Alamos Neutron Science Center, LANSCE, and the Spallation Neutron Source at Rutherford-Appleton Laboratory, ISIS). The investigated materials include a nickel-based alloy (IN718), an austenitic stainless steel (AISI 304L), a martensitic stainless steel (DIN 1.4926) and a refractory metal (Ta) which experienced 800 MeV proton irradiation to fluences of several 10 25  p/m 2 . The specimens were annealed from 300 °C to 700 °C for 1 to 10 h, respectively, and their mechanical property changes were subsequently investigated at room temperature and 250 °C by tensile testing and fracture surface analysis conducted by scanning electron microscopy (SEM). The results showed that the ductility recovered to a large degree in 304L and DIN 1.4926 materials while their strength remained almost unchanged. Especially for DIN 1.4926, the ductility recovery is remarkable already at 400 °C. Together with its favorable thermo-mechanical properties, this makes martensitic steel a candidate for structural materials of spallation targets.