Syntheses, morphology and dynamic mechanical properties of AB crosslinked polymers based on vinyl-terminated polyurethanes/allyl novolac resin

Vinyl-terminated polyurethane (VTPU) was prepared from the PU prepolymer and methacrylamide. The prepolymers were prepared by reacting 4,4′-diphenylmethane diisocyanate (MDI) with poly(tetramethylene oxide) (PTMO), whose molecular weight is Mn = 600–700 (this polymer is called VTU1) and Mn = 1900–2100 (VTU2), respectively. The AB crosslinked polymers (ABCPs) were synthesized from VTPU and allyl novolac resin, synthesized by substituting the hydroxy group of a phenolic resin with the allyl group. For these ABCPs, the phenomena of phase mixing was investigated and confirmed through dynamic mechanical analysis (DMA), differential scanning calorimetry (DSC) and transmission electron microscopy (TEM). The tensile strength of these ABCPs were improved and accorded with their structures and viscoelastic properties and morphology. Aus PU-Prapolymeren und Methacrylamid wurden vinyl-terminierte Polyurethane (VTPU) hergestellt. Fur die Synthese der Prapolymeren wurden 4,4′-Diphenylmethan-diisocyanat (MDI) und Poly(tetramethylenoxid) (PTMO) mit einem Molekulargewicht von Mn = 600–700 (VTU1) beziehungsweise von Mn = 1900–2100 (VTU2) eingesetzt. Die AB vernetzten Polymeren (ABCPs) wurden durch Reaktion von VTPU mit einem Allylnovolak-Harz hergestellt, das durch Substitution der Hydroxy-Gruppe des Phenolharzes mit einer Allylgruppe erhalten wurde. Fur diese ABCPs wurde das Phasenverhalten mit Hilfe der dynamisch-mechanischen Analyse (DMA), der Differential-Scanning-Kalorimetrie (DSC) und der Transmissionselektronenmikroskopie (TEM) untersucht. Die Zugfestigkeit der ABCPs konnte verbessert werden, was mit deren Struktur, den viskoelastischen Eigenschaften und der Morphologie in Einklang steht.