The effects of heat treatments on the microstructure and electrochemical properties of the ZrCr0.7Ni1.3 multiphase alloy
2001
Abstract Qualitative and quantitative X-ray analysis using the Rietveld method of the as cast ZrCr 0.7 Ni 1.3 alloy, shows an average phase abundance of 62.7% C15-Laves phase, 36.6% of Zr 7 Ni 10 and less than 1% of chromium. The annealed alloy at 1373 K reveals a complete disappearance of pure Cr with an important reduction of the amount of the Zr 7 Ni 10 phase based on EDS/SEM and XRD results. Pressure-Composition-Temperature (PCT) measurements show that the alloy behaves as a single phase with faster kinetics. Electrochemical measurements shows a relatively high discharge capacity of the cast alloy, c =320 mAhg −1 after 20 cycles. Contrary to that, the discharge capacity of the annealed alloy decreases by about a factor of 2 with c =156 mAhg −1 .