Synthesis and characterization of experimental endodontic sealers containing bioactive glasses particles of NbG or 45S5.

Abstract Objective This study evaluated the influence of adding bioactive glasses particles [Niobophosphate (NbG) or bioglass (45S5)] into endodontic cements in relation to physical, chemical and biological properties. Methods The following commercial cements were used as comparison: AH Plus (Dentsply), Endofill (Dentsply), MTA Fillapex (Angelus) and EndoSequence (BC Sealer, Brasseler). Setting time, radiopacity, flow rate, weight loss/variation, alkaline capacity (pH) at different time-intervals (24h/48h/7d/14d/28d), bioactivity (assessed under SEM/EDS, FTIR/ATR and XDR) and cell viability were measured. Data were analyzed by One-way ANOVA/Holm-Sidak post-test (α = 5%) (normal distribution) and Kruskal-Wallis/Students-Newman-Keuls post-test (α = 5%) (non-normal distribution). Results Bioactive endodontic experimental cements (containing NbG or 45S5) had high alkalinization capacity. The experimental cements presented high weight loss/variation (p  Significance The incorporation of bioactive particles (NbG or 45S5) into endodontic cements had potential to neutralize acidic environments and induced formation of hydroxyapatite precursors. Clinically, these would produce a cement that is bactericidal and have the potential to improve tissue healing. The improved radiopacity and flowability would facilitate the visualization of the material in the radiograph and the filling of anatomical complexities during root canal obturation. As drawbacks, the excessive weight loss and post-setting cytotoxicity could result in clinical degradation of the cement and adjacent tissue irritation for the patient.