Competitive effect of dopant concentration and the size of the nanorods over the electron phonon coupling in Cd doped ZnO nanorod arrays

Abstract Earlier reports on resonance Raman scattering in ZnO suggests that the electron phonon coupling in ZnO usually increase with nanoparticle size or decline with the doping concentration. We have investigated the effect of combination of the concentration of dopant and the variation of size of nanorods over the electron phonon interaction in Cd doped ZnO nanorod array fabricated by a simple, low temperature (90 °C) growth process. The resonant Raman measurement reveals minor decrease in the electron phonon coupling strength as defined by the intensity ratio (I2LO/I1LO) at low doping concentration (20 mol %) and increase at high Cd concentration (>20 mol %) confirming a strong dependence of electron phonon coupling strength on the concentration of dopant. But, the enhancement in the electron phonon coupling strength at high doping concentration is due to the increase in the diameter of the nanorod rather than the concentration of dopants confirming the competitive effect of dopant and size over the electron phonon interaction in a range of doping concentration. The Cd doping leads to the decrease in the band gap and the gradual increase (decrease) in the intensity of the excitonic emission (visible luminescence) as observed by the photoluminescence property. X-ray, fourier transform infrared (FTIR) analysis confirm low temperature doping of Cd at the tetrahedral coordination site of ZnO lattice Although, the Cd concentration in the growth solution is systematically varied from 1 mol % to 80 mol %, the maximum Cd doping concentration varies from 3 at. % (80 mol %) at the surface to 0.2 at % - 0.6 at. % in the bulk after surface cleaning by Ar ion etching.