Use of sputtered zinc oxide film on aluminium foil substrate to produce a flexible and low profile ultrasonic transducer.

Abstract A flexible and low profile ultrasonic transducer was fabricated for non-destructive testing (NDT) applications by DC sputtering of 3 μm thick, c -axis oriented, ZnO film on 50 μm aluminium foil. Due to the thin foil-based construction, the transducer can be applied to curved objects and used in sites of restricted accessibility. The device has been used to demonstrate detection of simulated defects in a 45 mm diameter steel pipe, and for thickness measurement on a 3.1 mm thick flat carbon steel plate. Centre frequency measured on the flat plate was 24–29 MHz, with −6 dB bandwidth 4–7 MHz. The pulse duration depended on the couplant, at best 3 cycles or 0.12 μs using SONO Ultragel or epoxy couplant. Transducer performance was found to be comparable to a commercial 10 MHz piezoelectric ultrasonic transducer.