Oxidation protection of carbon/carbon composites with a plasma-sprayed ZrB2–SiC–Si/Yb2SiO5/LaMgAl11O19 coating during thermal cycling
2015
Abstract Carbon/carbon composites were plasma sprayed with a ZrB 2 –SiC-Si/Yb 2 SiO 5 /LaMgAl 11 O 19 coating to improve the oxidation resistance at high temperature. Oxidation protection behavior of the coating was investigated by thermal cycling test using a gas flame about 2273 K. Results showed that the weight loss for the completely coated sample was only 0.30% after 10 cycles of heating for 79 min, and it gradually increased to 4.8% until the failure of coating with 24 cycles. The presence of through-cracks and horizontal cracks in the coating due to the durative oxidation of ZrB 2 –SiC–Si layer progressively accelerated the oxidation of substrate and failure of coating.