Influence of CdTe Deposition Temperature and Window Thickness on CdTe Grain Size and Lifetime After CdCl 2 Recrystallization

Grain structure influences both transport and recombination in CdTe solar cells. Larger grains generally are obtained with higher deposition temperatures, but commercially it is important to avoid softening soda-lime glass. Furthermore, depositing at lower temperatures can enable different substrates and reduced cost in the future. We examine how initial deposition temperatures and morphology influence grain size and lifetime after CdCl 2 recrystallization. Techniques are developed to estimate grain distribution quickly with low-cost optical microscopy, which compares well with electron backscatter diffraction data providing corroborative assessments of exposed CdTe grain structures. Average grain size increases as a function of CdCl 2 temperature. For lower temperature close-spaced sublimation CdTe depositions, there can be more stress and grain segregation during recrystallization. However, the resulting lifetimes and grain sizes are similar to high-temperature CdTe depositions. The grain structures and lifetimes are largely independent of the presence and/or interdiffusion of Se at the interface, before and after the CdCl 2 treatment.