Preparation of compact Li-doped Y2Ti2O7 solid electrolyte

Abstract Three series of solid electrolytes were prepared with the nominal compositions of (Y 2 − x Li 3x )Ti 2 O 7 (Y3LT), (Y 2 − x Li x )Ti 2 O 7 − x (YLT) and Y 2 − x Ti 2 O 7 − 3x/2 (YT) with x = 0.040 − 0.11. Comparing the unit cell a -axis of the YLT with that of YT, the latter is shorter with the same amount of x. This indicates a successful substitution of the Li ion into the Y site of Y 2 Ti 2 O 7 . However, both Y3LT and YLT have exactly the same unit cell a -axis length with the same amount of x so that the solid solution formed probably has the same formula, (Y 2 − x Li x )Ti 2 O 7 − x , in which only one Li ion is substituted into the Y site. Extra Li 2 O added in the Y3LT is probably acting as a self flux to lower the melting point of the mixture. As a result, materials become more compact and grains grow bigger. One compound of Y3LT with x = 0.060 has a total conductivity of 4.3(4) × 10 − 4  S⋅cm − 1 at 700 °C. Adding Li 2 O as a flux and carefully controlling the heat treatment history, compact sample of Y3LT with a relative density higher than 90% was obtained at a temperature as low as 1150 °C. Its ionic conductivity is comparable to one Y 2 Ti 2 O 7 prepared at 1600 °C with a conductivity reported as 2.30 × 10 − 4  S⋅cm − 1 .