Combined in situ neutron diffraction and acoustic emission of twin nucleation & twin growth in extruded ZM20 Mg alloy

In the present work in situ neutron diffraction and acoustic emission were used concurrently to study deformation twinning in two ZM20 Mg alloys with significantly different grain sizes at room temperature. The combination of these techniques allows differentionation between the twin nucleation and the twin growth mechanisms. It is shown, that yielding and immediate post-yielding plasticity in compression is governed primarily by twin nucleation, whereas the plasticity at higher strains is governed by twin growth. The current results further suggest that yielding by twinning happens in a slightly different manner in the fine-grained as compared to the coarse-grained alloy.