Recombination-Enhanced Effect in Green/Yellow Luminescence from BeZnCdSe Quantum Wells Grown by Molecular Beam Epitaxy

The recombination-enhanced defect reaction (REDR) effect in single green/yellow emission BeZnCdSe quantum wells (QWs) has been investigated using photoluminescence (PL) microscopy and time-resolved PL measurements. Even though a lattice hardening effect is expected in BeZnCdSe QWs alloyed with beryllium, PL intensity enhancement due to photoannealing as well as subsequent degradation due to generation of dark spot defects (DSDs) and dark line defects (DLDs) were observed. PL microscopy provided insights into the REDR effect during photoannealing. PL images were spatially inhomogeneous in intensity for the as-grown wafer, with the darker areas having size from submicrometer to 1 μm becoming brighter with the progress of photoannealing, revealing a built-in distribution of point defects incorporated in the structure during crystal growth. In addition, we showed that the PL lifetime increased with the progress of photoannealing; hence, the density of point defects decreased due to the REDR effect. A nonradiative decay channel insensitive to the REDR effect was also found in the area free from DSDs and DLDs, suggesting that another type of defect remained in the structure (note that this is not the defect reported in study of slow-mode degradation in long-lived laser diodes). As the degradation progresses, a nonradiative channel such as photocarrier diffusion and subsequent trapping by a patch of DLDs will emerge before radiative recombination.