In situ synchrotron X-ray imaging and mechanical properties characterization of additively manufactured high-entropy alloy composites

Abstract Laser beam directed energy deposition has become an increasingly popular advanced manufacturing technique for materials discovery as a result of the in situ alloying capability. In this study, we leverage an additive manufacturing enabled high throughput materials discovery approach to explore the composition space of a graded Wx(CoCrFeMnNi)100-x sample spanning 0 ≤ x ≤ 21 at.%. In addition to microstructural and mechanical characterization, synchrotron high speed x-ray computer aided tomography was conducted on a W20(CoCrFeMnNi)80 composition to visualize melting dynamics, powder-laser interactions, and remelting effects of previously consolidated material. Results reveal the formation of the Fe7W6 intermetallic phase at W concentrations > 6 at.%, despite the high configurational entropy. Unincorporated W particles also occured at W concentrations > 10 at.% accompanied by a dissolution band of Fe7W6 at the W/matrix interface and hardness values greater than 400 HV. The primary strengthening mechanism is attributed to the reinforcement of the Fe7W6 and W phases as a metal matrix composite. The in situ high speed x-ray imaging during remelting showed that an additional laser pass did not promote further mixing of the Fe7W6 or W phases suggesting that, despite the dissolution of the W into the Fe7W6 phase being thermodynamically favored, it is kinetically limited by the thickness/diffusivity of the intermetallic phase, and the rapid solidification of the laser-based process.