Cationic distribution assisted tuning of magnetic properties of Li0.5-x/2ZnxFe2.5-x/2O4

Zn addition induced modification of cationic distribution for tuning magnetic properties of Li0.5-x/2ZnxFe2.5-x/2O4 (x = 0, 0.1, 0.25, 0.3, 0.5, 0.7, 0.9, 1.0) powders is studied by x-ray diffraction (XRD) and, magnetic measurements. XRD shows the formation of cubic spinel structure, with Scherrer’s grain diameter ranging between 26.7 to 37.8 nm. With Zn addition, oxygen anions are displaced in such a way that the A-B interaction weakens, whereas A-A and B-B interaction strengthens; furthermore it also pushes Fe3+ and Li1+ ions to B site, leading to changes in magnetic properties. Highest saturation magnetization (Ms) of 64.6 A m2 / kg was obtained for sample with x = 0.25 and lowest coercivity (Hc) of 4949.9 A/m was obtained for the sample with x = 0.7. Calculated values of experimental magnetic moment ‘nB’ and Neel magnetic moment ‘nN’, display similar trend as that of Ms. Present results very clearly show a strong correlation between Zn-addition induced changes in cation distribution and magnetic prope...