Small Punch Testing of Sanicro 25 Steel and its Correlation with Uniaxial Tests

Small punch testing under constant deflection rate, constant force and constant deflection (i.e. force relaxation) were performed on the new austenitic steel Sanicro 25. Constant deflection rate experiments were correlated to uniaxial tensile tests at room temperature and 700°C with the help of several empirical relationships. Small punch creep testing was performed in as received state. Correlation of the small punch results with uniaxial creep test results was done and the force/stress ratio Ψ and kSP parameter were determined. The constant deflection small punch test was correlated with the uniaxial stress relaxation test and good agreement was reached.