Interfacial characteristics of N-incorporated HfAlO high-k thin films

The characteristics of N-incorporated HfO2–Al2O3 alloy films (HfAlO) were investigated by high-resolution x-ray photoelectron spectroscopy (XPS), near-edge x-ray absorption fine structure (NEXAFS), medium-energy ion scattering (MEIS), and capacitance–voltage measurements. The core-level energy states, Hf4f and Al2p peaks of a 15A thick film showed a shift to lower binding energy, resulting from the incorporation of nitrogen into the films. Absorption spectra of the OK edge of HfAlO were affected mainly by the Al2O3 in the film, and not by HfO2 after nitridation by NH3 annealing. The NEXAFS of NK edge and XPS data related to the chemical state suggested that the incorporated N atom is dominantly bonded to Al2O3, and not to HfO2. Moreover, MEIS results implied that there is a significant incorporation of N at the interface between the alloy film and Si. The incorporation of N effectively suppressed the leakage current without an increase in interfacial layer thickness, while the interfacial state of the N-i...