Effect of nano-TiB2 particles on the anisotropy in an AlSi10Mg alloy processed by selective laser melting

Abstract In components built by selective laser melting (SLM), possible anisotropy in microstructure significantly affects mechanical properties (i.e. service performance) and there is a constant effort to solve this problem. This work carried out a comparative study using fully dense AlSi10Mg alloy and in-situ nano-TiB 2 decorated AlSi10Mg composite samples processed by SLM. The aim was at clarifying the effect of integrated nanoparticles on the anisotropy of the as-built component. Microstructure and texture evolution were investigated by scanning and transmission electron microscopy, electron backscatter diffraction, X-ray and neutron diffraction. The SLMed AlSi10Mg sample shows a coarse columnar grain structure with and fiber orientation texture and obvious anisotropy in mechanical properties. However, the nano-TiB 2 modified AlSi10Mg sample exhibits fine equiaxed grains, no preferred crystallographic texture and remarkably reduced anisotropy. Besides, both tensile strength and ductility have been improved in the SLMed TiB 2 decorated AlSi10Mg sample. The preliminary mechanism upon grain refinement effect due to nano-TiB 2 particles on columnar-to-equiaxed transition and reduction of anisotropy was discussed.