Corrosion behavior of F82H exposed to high temperature pressurized water with a rotating apparatus

Abstract The present study reports the corrosion behavior of a reduced-activation ferritic martensitic steel F82H exposed to high temperature pressurized water for 28 and 100 h using a rotating disk apparatus at rotation speeds of 500 and 1000 rpm at a temperature of 573 K under a water pressure of 15 MPa with