30 mm wide process of GdBCO PLD/clad-type textured metal substrates

Abstract Gd 1 Ba 2 Cu 3 O x (GdBCO) coated conductors using bi-axially textured clad-type substrates have been developed for high temperatures superconducting (HTS) power cables. In this project, large amount of coated conductors (CCs) are necessary for the several tests of basic properties of HTS power cables and the fabrication of a 15 m long 3-in-one HTS model cable. In order to ensure an adequate amount and properties of coated conductors, the stable manufacturing technology and the high production rate at each process are required. In this report, we have newly installed a high power laser of 300 W for the PLD system, resulting in improvement of the manufacturing stability and the deposition rate for GdBCO film. In addition, we have optimized target–substrate distance in PLD process, and the uniformity of I c distribution across 30 mm wide tapes were remarkably improved. Furthermore, the surface morphology of buffer layers were enhanced by optimizing the deposition condition using electron beam (EB) evaporation method, and the maximum I c value for a short sample has achieved 497 A/cm at 77 K in the self-field. Based on these progresses, we are currently developing the stable manufacturing process for long CCs with over 400 A/cm.