SrO capping effect for La2O3/Ce-silicate gate dielectrics
2010
Abstract The chemical bonding states and electrical characteristics of SrO capped La 2 O 3 /CeO x gate dielectric have been examined. Angle-resolved X-ray photoelectron spectroscopy measurement has revealed that Sr atoms diffuse into silicate layer to form SrLa-silicate after annealing. Owing to the incorporation of Sr atoms into silicate layer, a transistor operation with an equivalent oxide thickness (EOT) below 0.5 nm has been demonstrated. A strongly degraded effective electron mobility of 78 cm 2 /V s at 1 MV/cm has been obtained, which fit well with the general trend in small EOT range below 1 nm. Although process optimization is needed to improve the performance of transistors, Sr capping technique can be useful for EOT scaling.